The effect of through-thickness compressive stress on mode II interlaminar fracture toughness
2017
Abstract The effect of through-thickness compressive stress on mode II interlaminar fracture toughness is investigated experimentally and replicated numerically. The modified Transverse Crack Tensile specimen recently proposed by the authors is used, together with an experimental device designed to apply a constant transverse compressive stress on the surface of the specimen. Experiments are conducted using IM7/8552 specimens for different compressive stresses, ranging from 0 to 100 MPa, covering all the practical applications commonly encountered in the aeronautical industry (e.g., tightened filled holes or bolted joints). It is shown that mode II interlaminar fracture toughness increases …
ELECTROSPUN NANOFIBROUS MATS IN FIBRE REINFORCED EPOXY LAMINATES
Hydrothermal aging of carbon reinforced epoxy laminates with nanofibrous mats as toughening interlayers
2016
Electrospun mats have been applied as toughening interlayers in high performance carbon fiber epoxy composites. While the toughening mechanism exerted by the mat at the interface is the subject of several recent studies, no investigations are reported on the aging behaviour of laminates comprising these nanostructured elements. This work investigates the influence of the combined effect of water and temperature (90 °C) on laminates with Nylon 6,6 electrospun membranes placed either at the middle plane only or at each interlayer. The water-uptake behaviour is modelled by a two-stage diffusion model and compared with the behaviour of the neat resin and of the laminate without mats. Interestin…
The effect of the through-the-thickness compressive stress on mode II interlaminar fracture toughness
2017
The effect of through-the-thickness compressive stress on the mode II interlaminar fracture toughness is investigated experimentally and replicated numerically. The modified Transverse Crack Tensile specimen recently proposed by the authors is used, together with an experimental device designed to apply a constant transverse compressive stress on the surface of the specimen. Experiments are conducted using IM7/8552 specimens for different compressive stresses, ranging from 0 to 100 MPa, covering all the practical applications commonly encountered in the aeronautical industry (e.g., tightened filled holes or bolted joints). It is shown that the mode II interlaminar fracture toughness increas…
Interlaminar fracture toughness behavior of electron-beam cured carbon-fiber reinforced epoxy-resin composites
2013
The work describes the preparation and physical-mechanical characterization of unidirectional CFRP panels manufactured by an electron beam curing technique. Delamination fracture toughness in Mode I and II is investigated in order to evaluate the influence of fiber–matrix adhesion strength, matrix toughness and matrix crosslinking density as determined by the radiation curing process. A matrix system comprising a DGEBA epoxy monomer and an initiator of cationic polymerization have been used, with one batch of resin mixed with a PES monomer in order to enhance matrix toughness. Curing was achieved with a pulsed 10 MeV Electron Beam accelerator. Thermally cured composite systems have also bee…
Mode I interlaminar fracture toughness of thin-ply laminates with CNT webs at the crack interface
2019
Abstract Pristine and functionalized carbon nanotube (CNT) webs were introduced at the interlaminar region of two different thin-ply carbon fibre reinforced polymer systems (NTPT 402 prepreg, and TeXtreme/SE84LV). The Mode I interlaminar fracture toughness (ILFT) for the NTPT 402 material was substantially lower. In contrast when SE84LV resin was used, the resistance curves were virtually unchanged and with no depreciation in the steady state value of the ILFT. This demonstrates that a careful choice of the resin is essential to permit the embedding of CNT webs in thin-ply laminates without compromising structural performance and opens a new way towards the development of multifunctional th…